Badadur® PBT8 TM-Z2
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Bada AG |
| Trademark: | Badadur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p3Qn2N_Badadur-PBT8-TM-Z2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Easy flowing standard injection moulding grade with very good mechanical properties, very high toughness |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.42 | % | |
| Equilibrium, 23°C, 50% RH | 0.18 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 1800 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Yield, 23°C) | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain 3(Yield, 23°C) | 5.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break 4(23°C) | > 50 | % | ISO 527-2/50 |
| Flexural Stress 5(23°C) | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 6 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) 8 | 223 | °C | ISO 3146 |
| CLTE 9 | DIN 53752 | ||
| Flow : 4.00 mm | 1.5E-4 | cm/cm/°C | |
| Transverse : 4.00 mm | 1.5E-4 | cm/cm/°C | |
| Maximum Service Temperature | IEC 216 | ||
| -- | 10020000 | °C | |
| some hours | 140 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 10 | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity 11 | > 1.0E+16 | ohms·cm | IEC 60093 |
| Relative Permittivity 12(1 MHz) | 3.30 | IEC 60250 | |
| Dissipation Factor 13(1 MHz) | 0.020 | IEC 60250 | |
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm 14 | HB | ||
| 1.60 mm 15 | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | Test Specimen accordng to ISO 3167, Type A |
| 5 . | 80x10x4 mm |
| 6 . | 80 x 10 x 4 mm |
| 7 . | 110x10x4mm |
| 8 . | Compound for moulding |
| 9 . | >=10x10x4 mm |
| 10 . | 80x80x1 mm |
| 11 . | 80x80x1 mm |
| 12 . | 80x80x1 mm |
| 13 . | 80x80x1 mm |
| 14 . | 125x13x.8 |
| 15 . | 125x13x1.6 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2937-67LG Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8716-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| FLEXCHEM™ 3551-02 | Colorite Polymers | PVC, Flexible | FLEXCHEM™ |
| LONOY lonoy 2100 LT | Kingfa | PC+PET | LONOY |
| PENTAMID B GV60 H natural | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |