DINALON® B1S25 C20-4172
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Grupo Repol |
| Trademark: | DINALON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p1rY0x_DINALON-B1S25-C20-4172.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DINALON® B1S25 C20-4172 is a Polyamide 6 (Nylon 6) product filled with 20% carbon fiber. It is available in Europe. Primary characteristic: conductive. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Humidity | < 0.25 | % | ISO 15512/B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 190 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.7 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 11000 | MPa | ISO 178 |
| Flexural Stress 2 | 240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 210 | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 200 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 245 to 275 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9870 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Stat-Rite® S408 | Lubrizol Advanced Materials, Inc. | Polyolefin, Unspecified | Stat-Rite® |
| KOPLA PC KBP1000 | KOPLA Co., Ltd. | PBT | KOPLA PC |
| LEXAN™ SFX173RU resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Pebax® Rnew 70R53 SP 01 | Arkema | PEBA-Ether | Pebax® Rnew |