PRE-ELEC® PA 1408
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p0kyAA_PRE-ELEC-PA-1408.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® PA 1408 is a conductive thermoplastic compound based on polyamide 6. Conductivity is achieved by using conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® PA 1408 has an excellent balance of mechanical properties and is easy to injection mould. Typical applications include injection moulded housings, boxes and technical parts. PRE- ELEC® PA 1408 is ideal for the applications where the good mechanical properties of polyamide are required. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.19 | g/cm³ | ASTM D792 |
| -- | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 270°C/5.0 kg | 0.70 | g/10 min | |
| 275°C/10.0 kg | 13 | g/10 min | |
| Molding Shrinkage - Flow | 1.6 to 2.2 | % | ASTM D955, ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 85 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 60.0 | MPa | ASTM D638, ISO 527-2 |
| -- | 50.0 | MPa | ASTM D638 |
| 4.00 mm | 50.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 9.0 | % | |
| Break, 4.00 mm | 45 | % | |
| Flexural Modulus | |||
| 4.00 mm | 1970 | MPa | ASTM D790 |
| 4.00 mm | 1900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1 | |||
| -20°C | 25 | kJ/m² | ASTM D256, ISO 179 |
| 23°C | 30 | kJ/m² | ISO 179 |
| 23°C | 27 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 2 | |||
| -20°C | No Break | ASTM D256, ISO 179 | |
| 23°C | No Break | ISO 179, ASTM D256 | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | 21.0 | kJ/m² | |
| 23°C, 4.00 mm | 50.4 | kJ/m² | |
| Notched Izod Impact Strength 3 | ISO 180 | ||
| -20°C | 20 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Unnotched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | No Break | ||
| 23°C, 4.00 mm | No Break | ||
| Unnotched Izod Impact Strength 4 | ISO 180 | ||
| -20°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 152 | °C | ASTM D648B, ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 60.0 | °C | ASTM D648A, ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 210 | °C | ASTM D1525, ISO 306/A50 3 5 |
| -- | 180 | °C | ASTM D1525, ISO 306/B50 4 6 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+8 | ohms | IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+7 | ohms·cm | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 280 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 80.0 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| 3 . | 4 mm thickness |
| 4 . | 4 mm thickness |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultralloy™ 3312 | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| Unichem 7000 | Colorite Polymers | PVC, Unspecified | Unichem |
| Nypol® PA A3 G50 HS RH PRTA012 NR439 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Braskem EVA CN8092 | Braskem | EVA | Braskem EVA |
| Honeywell PMP R1500 | Honeywell | PMP | Honeywell PMP |