Dryflex® V 60A101
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | ELASTO |
| Trademark: | Dryflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p0S1Zi_Dryflex-V-60A101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Dryflex V 60A001: Thermoplastic Elastomer Base Material: TPV Hardness: 60 Shore A Service Temperature: -50°C to +135°C Colour: Black, but available in any colour shade Presentation: Free flowing pellets. May require pre-drying before processing. Weather Resistance: Excellent Ozone-/UV- Resistance: Excellent Chemical Resistance: Excellent Recycling: 100% recyclable Mould Shrinkage (linear): Approx. 0.75 - 2% depending on e.g. shape of the detail and placement of gate |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ISO 2781 |
| Molding Shrinkage 1 | 0.75 to 2.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 15 sec) | 60 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| Across Flow : 100% Strain | 2.00 | MPa | |
| Flow : 100% Strain | 3.50 | MPa | |
| Tensile Stress | ISO 37 | ||
| Across Flow : Yield | 5.50 | MPa | |
| Flow : Yield | 3.50 | MPa | |
| Tensile Elongation | ISO 37 | ||
| Across Flow : Break | 520 | % | |
| Flow : Break | 120 | % | |
| Tear Strength 2 | ISO 34-1 | ||
| Across Flow | 19 | kN/m | |
| Flow | 20 | kN/m | |
| Compression Set 3 | ISO 815 | ||
| 23°C, 24 hr | 20 | % | |
| 70°C, 24 hr | 30 | % | |
| 100°C, 24 hr | 37 | % | |
| 125°C, 70 hr | 55 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (150°C, 168 hr) | 3.0 | % | ISO 37 |
| Change in Tensile Strain at Break in Air (150°C, 168 hr) | -9.0 | % | ISO 37 |
| Change in Shore Hardness in Air (Shore A, 150°C, 168 hr) | 4.0 | ISO 37 | |
| Change in Tensile Stress | ISO 37 | ||
| 125°C, 168 hr, in ASTM #1 Oil | -30 | % | |
| 125°C, 168 hr, in IRM 903 Oil | -49 | % | |
| Change in Tensile Strain at Break | ISO 37 | ||
| 125°C, 168 hr, in ASTM #1 Oil | -55 | % | |
| 125°C, 168 hr, in IRM 903 Oil | -67 | % | |
| Change in Shore Hardness | ISO 37 | ||
| Shore A, 125°C, 168 hr, in ASTM #1 Oil | -14 | ||
| Shore A, 125°C, 168 hr, in IRM 903 Oil | -29 | ||
| Change in Volume | ASTM D471 | ||
| 125°C, 168 hr, in ASTM Oil #1 | 40 | % | |
| 125°C, 168 hr, in IRM 903 Oil | 96 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | -50 to 135 | °C |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity | ASTM D3835 | ||
| 250 sec^-1 | 210 | Pa·s | |
| 1000 sec^-1 | 66.0 | Pa·s | |
| 5000 sec^-1 | 17.0 | Pa·s |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 180 to 220 | °C | |
| Middle Temperature | 180 to 220 | °C | |
| Front Temperature | 180 to 220 | °C | |
| Mold Temperature | 15.0 to 50.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 200 to 220 | °C | |
| Cylinder Zone 2 Temp. | 200 to 220 | °C | |
| Cylinder Zone 3 Temp. | 200 to 220 | °C | |
| Cylinder Zone 4 Temp. | 200 to 220 | °C | |
| Cylinder Zone 5 Temp. | 200 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | Depending on shape of the detail and placement of gate |
| 2 . | Method C, Crescent |
| 3 . | Type B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® B3 2 RM-D natural (3391) | AKRO-PLASTIC GmbH | Nylon 6+ABS | AKROMID® |
| Anjatech® R250-DT2/GF15 | Almaak International GmbH | Nylon 6 | Anjatech® |
| EPAMOULD 795A15 | Epaflex Polyurethanes S.R.L. | TPU-Polyether | EPAMOULD |
| Polygen SG8A | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |
| Versaflex™ GP 2810-70N | PolyOne Corporation | TPE | Versaflex™ |