Zytel® PLUS PLS93G35DH1 BK549
| Category: | Nylon 6 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® PLUS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p0Ngu4_Zytel-PLUS-PLS93G35DH1-BK549.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% Glass Reinforced, Heat Stabilized, Polyamide 6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.40 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.20 | -- | % | |
| Water Absorption (23°C, 24 hr, 2.00 mm) | 2.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12000 | 6500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 200 | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | 7.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 13 | -- | kJ/m² | |
| 23°C | 15 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | 80 | kJ/m² | |
| 23°C | 100 | 90 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 212 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 224 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 7.0E-6 | -- | cm/cm/°C | |
| Transverse | 1.0E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 6.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | 7.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (1.50 mm) | HB | -- | IEC 60695-11-10, -20 |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Melt Density | 1.24 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 2100 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.28 | -- | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrathane™ ALC-72D-B30 | Biomerics, LLC | TPU-PC | Quadrathane™ |
| TIPELIN® 7300B | MOL Petrochemicals Co. Ltd. | HDPE | TIPELIN® |
| WELLAMID Nylon 6000 GV 30 HW | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| COPYLENE® CM120LN | Phillips 66 | PP Impact Copolymer | COPYLENE® |
| Karina COMP. PVC IVORY -E 600D35/ 1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |