NEFTEKHIM ABS 0554E
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Nizhnekamskneftekhim Inc. |
| Trademark: | NEFTEKHIM ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p09zFb_NEFTEKHIM-ABS-0554E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS 0554 - is an extrusion grade with a good hardness and rigidity. It has a good flow characteristic and heat resistance required for production of extruded sheet. It is used for production of the sheets with a high surface quality (coextruded or not, with high extrusion ratio) intended for a wide range of applications, in refrigerators, sanitary, packaging, automotive components and furniture (profiles). It is produced self-colored only, free of additives and dye. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 3.5 to 6.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | |
| Water Absorption (Equilibrium) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 35.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 45 | % | ASTM D638 |
| Flexural Modulus | 2300 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 68.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | kJ/m² | DIN 53453 |
| Notched Izod Impact Strength (23°C) | 17 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ASTM D1525 1 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.17 | W/m/K | ASTM C177 |
| Deflection Temperature | 104 | °C | ASTM D648 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Styrene 2 | 0.050 | % | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-1 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 60 | ASTM D523 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| 2 . | Test Method: TU 2214-159-05766801-2011 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® AM650N | Reliance Industries Limited | PP Homopolymer | REPOL® |
| REXtac® APAO RT 2304 | Huntsman Corporation | PAO | REXtac® APAO |
| Adstif HA5009 | LyondellBasell Industries | PP Homopolymer | Adstif |
| GECET™ 5501 | Fagerdala USA Inc. | PS (EPS) | GECET™ |
| Dryflex® VE 80A101 | ELASTO | TPV | Dryflex® |