LNP™ THERMOCOMP™ BF004 compound
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p05H6U_LNP-THERMOCOMP-BF004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP BF004 is a compound based on SAN resin containing 20% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound BF-1004 Product reorder name: BF004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.30 to 0.50 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.19 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.26 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8270 | MPa | ASTM D638 |
| -- | 8230 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 108 | MPa | ASTM D638 |
| Break | 103 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.7 | % | ASTM D638 |
| Break | 1.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 7590 | MPa | ASTM D790 |
| -- 5 | 7290 | MPa | ISO 178 |
| Flexural Strength 6(Break, 50.0 mm Span) | 140 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 35 | J/m | ASTM D256 |
| 23°C 7 | 3.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 200 | J/m | ASTM D4812 |
| 23°C 8 | 13 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 7.50 | J | ASTM D3763 |
| -- | 1.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 104 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 104 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 100 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 100 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.4E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 4.7E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*3 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoPrene 90A-4000 | KMI Group Inc. | TPV Alloy | PrimoPrene |
| Ravaflex BIIR | Ravago Group | BIIR | Ravaflex |
| Multi-Flex® TPE A6202 MR | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| Koylene SM250N | Reliance Industries Limited | PP Homopolymer | Koylene |
| Hytrel® PC945 NC010 | DuPont Performance Polymers | TPC-ET | Hytrel® |