Lucky Enpla LAY3003R is a polycarbonate polybutene terephthalate (PC PBT) product,. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.70 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 58.8 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2160 | MPa | ASTM D790 |
| Flexural Strength 3 | 86.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | ASTM D256 | ||
| -30°C, 3.18 mm | 130 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 740 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 103 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 240 - 270 | °C | |
| Middle Temperature | 250 - 270 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Nozzle Temperature | 260 - 280 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Back Pressure | 0.490 - 1.47 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Injection instructions |
|---|
| Resin Temperature: 250-270°CInjection Pressure (1st Pressure): 800-1200 kg/cm²Injection Pressure (2nd Pressure): 500-800 kg/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 10 mm/min |
| 3 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cri-Line TFEP-820 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Ferro PP TPP20AE55BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Geon™ Vinyl Flexible 90051 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| POLYFORT® FPP 10 GFC | A. Schulman Europe | PP Homopolymer | POLYFORT® |
| Sylvin 9604-90 White 1118 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |