LNP™ THERMOCOMP™ IF003 compound
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oxLykg_LNP-THERMOCOMP-IF003-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* IF003 is a compound based on Nylon 6/12 resin containing 15% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound IF-1003 Product reorder name: IF003 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.40 to 0.60 | % | ASTM D955, ISO 294-4 |
| Across Flow : 24 hr | 1.0 to 1.2 | % | ASTM D955 |
| Across Flow : 24 hr | 1.0 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.22 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.26 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5540 | MPa | ASTM D638 |
| -- | 5430 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 101 | MPa | ASTM D638 |
| Break | 99.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.6 | % | ASTM D638 |
| Break | 2.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5210 | MPa | ASTM D790 |
| -- | 4590 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 164 | MPa | ASTM D790 |
| -- | 157 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 2 | 4.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 240 | J/m | ASTM D4812 |
| 23°C 3 | 22 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.20 | J | ASTM D3763 |
| -- | 1.83 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 192 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 181 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 4.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 8.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 8.1E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 254 to 266 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnamid® T- 27 MW 30 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Fireguard® 910L16-C14-NL | Teknor Apex Company | PVC, Flexible | Fireguard® |
| Durepol® PBT A3 G30 PRTA011 BT304 MSP | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
| SIBUR Synthetic Rubber SBR-1705 Group I | SIBUR | SBR, Emulsion | SIBUR Synthetic Rubber |
| LNP™ LUBRILOY™ R2000 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |