LNP™ THERMOCOMP™ ZX08005 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | owhH0m_LNP-THERMOCOMP-ZX08005-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP ZX08005 is a Compound based on PPE + PS Blend resin, containing Mineral. Added features include: Improved Dielectric Properties. Also known as: LNP* THERMOCOMP* Compound ZX08005 Product reorder name: ZX08005 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.07 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 55.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.4 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 4600 | MPa | ISO 178 |
| Flexural Stress | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 17 | kJ/m² | ISO 180/1U |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Relative Permittivity | IEC 60250 | ||
| 100 MHz | 6.58 | ||
| 500 MHz | 6.47 | ||
| 1.00 GHz | 6.16 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 MHz | 1.0E-3 | ||
| 500 MHz | 1.0E-3 | ||
| 1.00 GHz | 1.0E-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 277 to 288 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 299 to 310 | °C | |
| Processing (Melt) Temp | 299 to 304 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong Nylon PA1212BR-3 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon, Unspecified | Shandong Nylon |
| VAMPTER 3026 V0 | Vamp Tech | PBT | VAMPTER |
| JSR EPR EP961SP | JSR Corporation | EPDM | JSR EPR |
| Magnobond 8005 | Magnolia Plastics, Inc. | Epoxy | Magnobond |
| Sylvin 916VO-90 Grey 9459 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |