SCLAIR® 19H
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | SCLAIR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | owds8X_SCLAIR-19H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SCLAIR®19H is a high density polyethylene material,. This product is available in North America and is processed by film extrusion or coextrusion. SCLAIR®The main features of 19H are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.38 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 68 | ASTM D2240 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 830 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 1330 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 26.0 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 23.0 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 53.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 23.0 | MPa | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 18 | g | ASTM D1922 |
| TD : 38 µm, blown film | 1800 | g | ASTM D1922 |
| Oxygen Transmission Rate (23°C, 0% RH, 38 µm, blown film) | 1700 | cm³/m²/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (38°C, 100% RH, 38 µm, Blown Film) | 4.2 | g/m²/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 129 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 5 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 81 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Friction Puncture - Blown Film (38.0 µm) | 300 | J/cm | Internal method |
| Extrusion instructions |
|---|
| Blow-up Ratio: 5.5:1 to 4:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1387 TFE 10 L | RTP Company | PPS | RTP |
| Toughblend® AS-1400 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | AS | Toughblend® |
| Aristech ALTAIR PLUS® (0.275 inch) | Aristech Acrylics LLC | ABS+Acrylic | Aristech |
| Karina WHITE PVC COMPOUND -E 820-10/ 1-D-TR | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ DFL34 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |