KRYSTALFLEX™ PE499
| Category: | PUR-Eth,aliphat , Polyurethane (Polyether, Aliphatic) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | KRYSTALFLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | owQP9I_KRYSTALFLEX-PE499.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KRYSTALFLEX PE499 is a high performance aliphatic polyether film intended for processing by lamination into a range of glass/plastics components. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 65 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% strain | 1.72 | MPa | ASTM D412 |
| 300% strain | 2.76 | MPa | ASTM D412 |
| Tensile Strength 2(Yield) | 24.1 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 850 | % | ASTM D412 |
| Tear Strength | 39.4 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -48.9 | °C | DSC |
| Additional Information |
|---|
| Softening Range, TMA: 140 to 230°FTypical Laminating Parameters:Ultimate Temperature: 194 to 212°FUltimate Pressure: 116 to 174 psiSoaking Time: 30 min/0.25 in |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 285 HS | RTP Company | Nylon 66 | RTP |
| Ultrason® E 3010 MR UN | BASF Corporation | PESU | Ultrason® E |
| DESLON™ 6 DSC121HI | DESCO Co., Ltd. | Nylon 6 | DESLON™ 6 |
| DILAMID® 6 FVT 30 BLACK | Dilaplast S.p.A. | Nylon 6 | DILAMID® |
| LUVOCOM® 80-8030 VP | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |