Radilon® S USX270 333 NER
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ovHa6g_Radilon-S-USX270-333-NER.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA6 extrusion grade. Toughened. Black colour. Suitable for extrusion of parts requiring excellent impact resistance and very high flexibility. ISO 1043 : PA6-HI |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.11 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C, 2.00 mm | 7.0 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.8 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1300 | 600 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 35.0 | 20.0 | MPa | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | > 100 | > 100 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 1200 | 500 | MPa | ISO 178 |
| Flexural Stress 2 | 40.0 | 18.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 30 | -- | kJ/m² | |
| 23°C | 70 | 120 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 80.0 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 50.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 105 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 220 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | < 30 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm) | 675 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Melt Temperature | 240 to 270 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Teflon® PTFE 6C X | DuPont Fluoropolymers | PTFE | Teflon® PTFE |
| Sumikon® FM-MK115S | Sumitomo Bakelite Co., Ltd. | PPS | Sumikon® |
| UNIVAL™ DMDB-6200 NT 7 | The Dow Chemical Company | HDPE | UNIVAL™ |
| Ecodear® V911X51 | Toray Resin Company | PLA | Ecodear® |
| Lupol® GP3209A | LG Chem Ltd. | TPO | Lupol® |