Visiloy™ 2615R11U2
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Technical Polymers, LLC |
| Trademark: | Visiloy™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ouTUkq_Visiloy-2615R11U2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Visiloy™ 2615R11U2 is a Polycarbonate + PBT (PC+PBT) material filled with 11% glass fiber. It is available in North America for extrusion or injection molding. Important attributes of Visiloy™ 2615R11U2 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 86.2 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 4.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 3790 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 116 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 282 | °C | |
| Mold Temperature | 65.6 to 98.9 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 80 | rpm | |
| Clamp Tonnage | 4.1 to 8.3 | kN/cm² | |
| Cushion | 3.18 to 6.35 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 to 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultraform® N 2720 M63 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Escorene™ Ultra FL 00014 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Delene 2030 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |
| TECHNYL STAR® SX 216 V50 BLACK | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR® |
| Sylvin 8950-85 NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |