Multi-Flex® TPE A7727 HM
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Multibase, A Dow Corning Company |
| Trademark: | Multi-Flex® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | otieQw_Multi-Flex-TPE-A7727-HM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Multi-Flex® TPE A7727 HM is a Thermoplastic Elastomer (TPE) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 10 sec) | 44 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 393 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 9.65 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 490 | % | ASTM D412 |
| Tear Strength | 68.3 | kN/m | ASTM D624 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 182 | °C | |
| Middle Temperature | 191 | °C | |
| Front Temperature | 199 | °C | |
| Nozzle Temperature | 204 | °C | |
| Processing (Melt) Temp | 204 | °C | |
| Mold Temperature | 26.7 to 37.8 | °C | |
| Injection Rate | Moderate-Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1200 S-65D | RTP Company | TPU-Polyester | RTP |
| TAROLOX GFR | Taro Plast S.p.A. | PBT | TAROLOX |
| Elastocon® 8150B | Elastocon TPE Technologies | TPE | Elastocon® |
| KEP® 270 | Kumho Polychem Co., Ltd. | EPDM | KEP® |
| Luxus PP 16303 | Luxus Limited | PP, Unspecified | Luxus PP |