Monprene® CP-19141
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Monprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ot2ZiC_Monprene-CP-19141.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Monprene®CP-19141 is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. Monprene®The main features of the CP-19141 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.908 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (150°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 second, injection molding | 45 | ASTM D2240 | |
| Shore A, 5 seconds, injection molding | 42 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain 1 | 0.779 | MPa | ASTM D412 |
| Flow : 100% strain 2 | 3.13 | MPa | ASTM D412 |
| Transverse flow : 300% strain 3 | 1.64 | MPa | ASTM D412 |
| Flow : 300% strain 4 | 4.77 | MPa | ASTM D412 |
| Tensile Strength 5 | ASTM D412 | ||
| Transverse flow : Fracture | 13.1 | MPa | ASTM D412 |
| Flow : Fracture | 6.81 | MPa | ASTM D412 |
| Tensile Elongation 6 | ASTM D412 | ||
| Transverse flow : Fracture | 560 | % | ASTM D412 |
| Flow : Fracture | 620 | % | ASTM D412 |
| Tear Strength 7 | ASTM D624 | ||
| Transverse flow | 42.4 | kN/m | ASTM D624 |
| Flow | 27.3 | kN/m | ASTM D624 |
| Compression Set 8(23°C, 22 hr) | 17 | % | ASTM D395B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 182 - 232 | °C | |
| Middle Temperature | 188 - 238 | °C | |
| Front Temperature | 193 - 243 | °C | |
| Nozzle Temperature | 199 - 249 | °C | |
| Processing (Melt) Temp | 199 - 249 | °C | |
| Mold Temperature | 10.0 - 32.2 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。 |
| Note Message | |
|---|---|
| 1 . | Mouth die C, 510mm/min |
| 2 . | Mouth die C, 510mm/min |
| 3 . | C mold, 510mm/min |
| 4 . | C mold, 510mm/min |
| 5 . | C mold, 510mm/min |
| 6 . | Mouth die C, 510mm/min |
| 7 . | C mold, 510mm/min |
| 8 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WMB 127M | Pooya Polymer Tehran | Polyolefin, Unspecified | WMB |
| UNITIKA Nylon 66 E-RUNG60 | UNITIKA Plastics Division | Nylon 66 | UNITIKA Nylon 66 |
| Elastollan® C 75 A HPM | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Karina IVORY PVC COMP. -E 850-35/ 1-C | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SABIC® EPDM 756 | Saudi Basic Industries Corporation (SABIC) | EPDM | SABIC® EPDM |