ALCUDIA® EBA PA-303
| Category: | EBA , Ethylene Butyl Acrylate Copolymer |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® EBA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | osiKrW_ALCUDIA-EBA-PA-303.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EBA ALCUDIA® PA-303 is a copolymer suitable for blown film applications with good optical and mechanical properties even at low temperatures. The material has very good sealing properties. The butyl acrylate content is 3%. TYPICAL APPLICATIONS
Recommended melt temperature 180°C. Processing characteristics of PA-303 are similar to LDPE and conventional polyethylene extruders are recommended. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| n-Butyl Acrylate Content | 3.0 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 130 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Fracture, 130 µm, blown film | 25.0 | MPa | ISO 527-3 |
| TD : Fracture, 130 µm, blown film | 25.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture, 130 µm, blown film | 500 | % | ISO 527-3 |
| TD : Fracture, 130 µm, blown film | 700 | % | ISO 527-3 |
| Dart Drop Impact (130 µm, Blown Film) | 600 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 130 µm, blown film | 4.0 | N | ISO 6383-2 |
| TD : 130 µm, blown film | 6.0 | N | ISO 6383-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45 °, 125 µm, blown film) | 70 | ASTM D2457 | |
| Haze (125 µm, blown film) | 10 | % | ASTM D1003 |
| Additional Information |
|---|
| Data taken from 125 µm thickness film, blow up ratio 1:2.5, frost line height 50 cm. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fainplast PVC PK 6010 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Sylvin 8250-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 7011EE-72 WHITE 1277 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Iupilon® HL-3503 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| LinGen FR345 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TEEE | LinGen |