Chemical Resources PP 3000 REP
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Chemical Resources, Inc. |
| Trademark: | Chemical Resources |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | osLeok_Chemical-Resources-PP-3000-REP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A polypropylene homopolymer produced using metallocene catalyst technology. Provides lower extractables and better clarity than conventional homopolymers. This product is in pellet form. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 34 | g/10 min | ASTM D1238 |
| Molecular Weight Distribution | 1.80 | Mw/Mn |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 31.7 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield) | 9.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3 | 1250 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 21 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 93.9 | °C | ASTM D648 |
| Melting Temperature | 149 | °C | DSC |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirathane™ E185 | Miracll Chemicals Co., Ltd. | TPU-Polyester | Mirathane™ |
| Bergamid™ B70 G10 H BK702 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| ICORENE® N1018 | ICO Polymers EMEA, A Division of A. Schulman | EVA | ICORENE® |
| LONGLITE® LCP LCP-300 B3G | CCP Group | LCP | LONGLITE® LCP |
| Plaslube® PPA GF30 TL15 | Techmer Engineered Solutions | PPA | Plaslube® |