Aurora PVC AP1085 Series AAMA
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Aurora Plastics, Inc. |
| Trademark: | Aurora PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | os5ZsA_Aurora-PVC-AP1085-Series-AAMA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A high rate, midrange gloss, PVC powder, extrusion compound for exterior/interior applications. Typical test results for ASTM D-4216. This is a Rigid PVC formulation per the requirements of AAMA 303-05. Testing was performed on actual window parts with a wall thickness of 0.100". This material meets/exceeds cell class 1-20131-13**as required in ASTM D-4726. Testing was performed by Dallas Laboratory, Inc., July 2006. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 to 1.47 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 1-43344-12 | ASTM D4216 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 1(Shore D, 22°C) | 75 to 81 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (22°C) | 3010 | MPa | ASTM D638 |
| Tensile Strength (Yield, 22°C) | 46.2 | MPa | ASTM D638 |
| Flexural Modulus (22°C) | 2650 | MPa | ASTM D790 |
| Flexural Strength (22°C) | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (22°C) | 980 | J/m | ASTM D256 |
| Drop Impact Resistance | ASTM D4226 | ||
| 22°C, Extruded at 370 to 380° F melt temperature 2 | > 120 | J/cm | |
| 22°C, Extruded at 370 to 380° F melt temperature 3 | > 120 | J/cm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 70.6 | °C | ASTM D648 |
| CLTE - Flow (22°C) | 5.2E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | ASTM D635 | ||
| (AEB)Avg.Extent of Burning | < 5.00 | mm | |
| (ATB)Avg.Time of Burning : 2.54 mm | < 5.0 | sec |
| Note Message | |
|---|---|
| 1 . | Instantaneous |
| 2 . | Procedure A |
| 3 . | Procedure B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 523P | SABIC Americas, Inc. | PP Homopolymer | SABIC® PP |
| Stat-Rite® S-102 | Lubrizol Advanced Materials, Inc. | PE Alloy | Stat-Rite® |
| Sup-tech AE704 | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon+PPE | Sup-tech |
| Wanthane® WHT-2190 | Wanhua Chemical Group Co., Ltd. | TPU-Capro | Wanthane® |
| Andur 2-920 AP | Anderson Development Company | PUR-Est/eth,TDI | Andur |