OnForce™ LFT UR-50 LGF/000 Natural

Category:	PUR, Unspecified , Polyurethane
Manufacturer:	PolyOne Corporation
Trademark:	OnForce™ LFT
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	orWS4K_OnForce-LFT-UR-50-LGF-000-Natural.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Polyvan's long fiber thermoplastic polymers are used in situations where high hardness and good impact resistance are required, such as metal substitution or other structural applications. These products exhibit enhanced physical and mechanical properties compared to staple fiber products. Its advantages include improved impact strength, elasticity and material strength in different temperature ranges. In addition, compared with traditional high-filled short fiber products, long fiber thermoplastic polymers show improved properties in terms of creep and fatigue resistance, improved dimensional stability and unique surface finish.

General Information
Filler / Reinforcement	Long glass fiber, 50% filler by weight
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.60	g/cm³	ASTM D792
Molding Shrinkage - Flow	0.10 - 0.20	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus ¹	14500	MPa	ASTM D638
Tensile Strength (Yield)	241	MPa	ASTM D638
Tensile Elongation ²(Break)	2.0 - 3.0	%	ASTM D638
Flexural Modulus	15200	MPa	ASTM D790
Flexural Strength (Yield)	352	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, 3.18 mm, Injection Molded)	450	J/m	ASTM D256
Unnotched Izod Impact	1600	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	114	°C	ASTM D648

Injection	Nominal Value	Unit
Drying Temperature	90.0	°C
Drying Time	8.0 - 12	hr
Processing (Melt) Temp	230 - 250	°C
Mold Temperature	80.0	°C

Injection instructions
LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.This grade must be dried in a dessicant dryer with a dew point set at -40°C.

Injection instructions

LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.This grade must be dried in a dessicant dryer with a dew point set at -40°C.

Note Message
1 .	Type 1, 5.1 mm/min
2 .	Type 1, 5.1 mm/min

Resin Grade	Manufacturer	Category	Trademark
Vi-Chem PVC V220-80E	Vi-Chem Corporation	PVC, Unspecified	Vi-Chem PVC
Trademark PE LLD2025G	Trademark Plastics Corporation	LLDPE	Trademark PE
Ultramid® 8202C HS BK-102	BASF Corporation	Nylon 6	Ultramid®
INSULCAST® RTVS 3-95-2	ITW Polymers Coatings North America	Silicone Rubber, RTV-2	INSULCAST® RTVS
Sylvin 8940-95 Red 6272	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin