Total Petrochemicals PPR 3260 is a random copolymer polypropylene with a Melt Flow Index of 1,8 g/10 min suitable for extrusion applications and for the manufacturing of films with easy heat weldability in the blown process. Polypropylene PPR 3221 is intended for the production of flexible packaging. It can also be used as in internal non-adhesive layer in coextruded PE based hood structures. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.902 | g/cm³ | ISO 1183 |
| Apparent Density | 0.53 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.8 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 84 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 26.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2 |
| Flexural Modulus | 1000 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress - MD | ISO 527-3 | ||
| Yield, 40 µm, Blown Film | 33.0 | MPa | |
| Break, 10 µm, Blown Film | 76.0 | MPa | |
| Tensile Elongation - MD (Break, 50 µm, Blown Film) | 650 | % | ISO 527-3 |
| Dart Drop Impact (40 µm, Blown Film) | 36 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 40.0 µm | 3.0 | kN/m | |
| TD : 40.0 µm | 13.0 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.5 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 7.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 130 | °C | ISO 306/A50 |
| -- | 67.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 148 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (40.0 µm, Blown Film) | 33 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 19 | % | ISO 14782 |
| Note Message | |
|---|---|
| 1 . | Blown FIlm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STYRON A-TECH™ 1260 | Americas Styrenics LLC | PS (HIPS) | STYRON A-TECH™ |
| Adell Polyamide AN-38 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Chemraz 629 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| CALIBRE™ 351-22 | Sumika Styron Polycarbonate Limited | PC | CALIBRE™ |
| Thermec N™ 4340R35F4 | Technical Polymers, LLC | PPA | Thermec N™ |