XENOY™ X2203 resin
| Category: | ABS+PBT+PC , Acrylonitrile Butadiene Styrene + PBT + PC |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | opo64Z_XENOY-X2203-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Xenoy product that provides improved chemical resistance and impact performance versus previous generation X2202 product which is used in the market spaces such as soap dispenser, cleaning equipment, filter housing |
| General Information | |
|---|---|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Volume-Flow Rate (MVR) (265°C/5.0 kg) | 35.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus 1(50.0 mm Span) | 2650 | MPa | ASTM D790 |
| Flexural Strength 2(Yield, 50.0 mm Span) | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 130 | J/m | |
| 0°C | 120 | J/m | |
| 23°C | 210 | J/m | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -20°C, Total Energy | 72.0 | J | |
| 0°C, Total Energy | 67.0 | J | |
| 23°C, Total Energy | 68.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 103 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 90.0 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 50 to 80 | % | |
| Rear Temperature | 249 to 271 | °C | |
| Middle Temperature | 254 to 277 | °C | |
| Front Temperature | 260 to 282 | °C | |
| Nozzle Temperature | 254 to 277 | °C | |
| Processing (Melt) Temp | 260 to 282 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.552 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.013 to 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYNIL® P50 H | Nilit Plastics | Nylon 66 | POLYNIL® |
| Multiuse Leostomer® LJ-3180N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| COPYLENE® CH085 | Phillips 66 | PP Homopolymer | COPYLENE® |
| Hybrid S464G5 | Ravago Manufacturing Americas, LLC | PC+ABS | Hybrid |
| Karina GREEN COLOR CONCENTRATE 40/130-FC-LMP (SDB) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |