BJB Polyurethane WC-783 A/B
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ooGQxD_BJB-Polyurethane-WC-783-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| WC-783 A/B is an impact resistant, rigid, 82 Shore D material that is commonly used to make clear or tinted castings of all kinds. When used at room temperature, castings 1/8" thick or larger can be readily cast. Castings that are less than 1/8" thick generally require a mild post-cure. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Specific Gravity | |||
| Part A | 1.057 | g/cm³ | |
| Part B | 1.027 | g/cm³ | |
| Shrinkage | |||
| -- 1 | 0.20 | % | |
| -- 2 | 0.20 | % | |
| -- 3 | 0.20 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion (-20 to 130°C) | 9.00E-5 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Demold Time (25°C) | 6.0 to 8.0 | hr | |
| Work Time (25°C) 4 | 15.0 | min |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Brookfield Viscosity | |||
| Mixed : 25°C | 600 to 700 | mPa·s | |
| Part A : 25°C | 550 to 650 | mPa·s | |
| Part B : 25°C | 550 | mPa·s |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Cure Time (25°C) 5 | 5.0 to 7.0 | day |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 to 84 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1790 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 45.9 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 65 | % | ASTM D638 |
| Flexural Modulus | 2210 | MPa | ASTM D790 |
| Flexural Strength | 75.8 | MPa | ASTM D790 |
| Compressive Modulus | 2410 | MPa | ASTM D695 |
| Compressive Strength | 57.6 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 70.0 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 90, Mix Ratio by Volume: 93 | ||
| Shelf Life | 26 | wk |
| Note Message | |
|---|---|
| 1 . | 12"x1/2"x1/2", 5 min work time |
| 2 . | 12"x1/2"x1/2", 15 min work time |
| 3 . | 12"x1/2"x1/2", 30 min work time |
| 4 . | 100g |
| 5 . | For maximum physical properties, a post cure with heat is required (16 hrs at 180°F). Cure will be inhibited if cast against a tin catalyzed silicone RTV. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TIPPLEN® H 649 FH | MOL Petrochemicals Co. Ltd. | PP Homopolymer | TIPPLEN® |
| Trexprene® D40BW | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| DOW™ LDPE 133A | The Dow Chemical Company | LDPE | DOW™ LDPE |
| Hifax TYC 1123X | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| HiFill® MD PA66 0125 LE | Techmer Engineered Solutions | Nylon 66 | HiFill® |