HANWHA CLNA TR-8142EC
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oo4vuR_HANWHA-CLNA-TR-8142EC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hanwha Wire and Cable Compound CLNA TR-8142EC is a water tree retardant low density, crosslinkable polyethylene compound designed for medium voltage power cable insulation in service involving exposure to water. It has a extremely low level of contamination and proper balance of non-staining antioxidant and peroxide to ensure thermal stability and optimum cure levels |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Degree of Crosslinking | 82 | % | ASTM D2765A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset | 75 | % | IEC 60811-2-1 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Relative Bow-tie Tree Size 1 | % | Internal method | |
| Resistance to Water Tree Growth - 30 days 2(25°C) | % | ASTM D6097 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 50 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 19.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 550 | % | ASTM D638 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (150°C, 360 hr) | < 15 | % | ASTM D573 |
| Change in Ultimate Elongation in Air (150°C, 360 hr) | < 15 | % | ASTM D573 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.28 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 5.0E-4 | ASTM D150 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 115 - 130 | °C |
| Extrusion instructions |
|---|
| Cure Temperature : 320-390°CLine Speed : 3-8 m/min |
| Note Message | |
|---|---|
| 1 . | Tree test conditions: Frequency=1kHz, Applied Voltage=5kV, 0.01M NaCl Solution. |
| 2 . | Tree test conditions: Frequency=1kHz, Applied Voltage=5kV, 0.01M NaCl Solution. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-110 | Teknor Apex Company | TPE | Medalist® |
| TYNE® Olefins W7124 | Tyne Plastics LLC. | PP Copolymer | TYNE® Olefins |
| NatureFlex™ NVS 120 | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| CP PRYME® Nylon 66 NN333HSL BK-P | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |
| OTECH PVC OE8033 - Calendering | OTECH Corporation | PVC, Unspecified | OTECH PVC |