| HF380 ABS: General Purpose High Flow Grade |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 4.0 | g/10 min | |
| 220°C/10.0 kg | 43 | g/10 min | |
| 230°C/3.8 kg | 15 | g/10 min | |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 106 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 44.4 | MPa | ASTM D638 |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | > 5.0 | % | |
| Break | > 10 | % | |
| Flexural Modulus 3 | 2420 | MPa | ASTM D790 |
| Flexural Strength 4 | 71.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 120 | J/m | |
| -30°C, 6.40 mm | 120 | J/m | |
| 23°C, 3.20 mm | 260 | J/m | |
| 23°C, 6.40 mm | 250 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 89.0 | °C | |
| 0.45 MPa, Annealed, 6.40 mm | 91.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 86.0 | °C | |
| 1.8 MPa, Annealed, 6.40 mm | 90.0 | °C | |
| Vicat Softening Temperature | 94.0 | °C | ASTM D1525 5 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Flammability (3.20 mm) | FH3-35 | mm/min | IEC 707 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 2500-4 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| WEVO-CHEMIE Polyurethanes PU 590 FL/300 M | WEVO-CHEMIE GmbH | PUR, Unspecified | WEVO-CHEMIE Polyurethanes |
| ALCOM® PA66 910/1.1 CF10 GF10 IM | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| Diakon® CMH454 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| KEBAFORM® C 1090 | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |