MAJORIS DFR110
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ong7Yc_MAJORIS-DFR110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DFR110 is a halogen free flame retardant compound with 10 % glass fibre reinforced UL 94 V0 intended for injection moulding. The product is available in natural (DFR110) but other colours can be supplied on request. DFR110 produces very low level of toxicity and low smoke density in the case of a fire. APPLICATIONS DFR110 has been developed especially for very demanding applications in automotive industry and electrical parts (conform 2002/95/EC, RoHS directive).
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.90 - 1.1 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2900 | MPa | ISO 178 |
| Flexural Stress 2 | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 28 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 125 | °C | ISO 75-2/A |
| Ball Pressure Test (135°C) | Pass | NF C 61-303 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | UL 94 | |
| 1.60 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 - 240 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKANATE™ G720 | Mando Advanced Materials Co., Ltd. | PC | TEKANATE™ |
| Cereplast Compostables® 2001 | Cereplast, Inc. | PLA | Cereplast Compostables® |
| Fainplast PVC RST 0413 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Kynar® 740 | Arkema | PVDF | Kynar® |
| RONFALIN® ABS 1334 | A. Schulman Europe | ABS | RONFALIN® |