Generic PBT+ASA - Glass Fiber
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | omdnQ8_Generic-PBT-ASA---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PBT+ASA - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.30 - 1.51 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 - 0.85 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 19.7 - 35.1 | cm³/10min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.18 - 1.1 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.40 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.10 - 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4910 - 10200 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 98.3 - 126 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 - 3.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4010 - 9800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 139 - 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 - 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 39 - 55 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 9.9 - 11 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 40 - 50 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 204 - 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 148 - 200 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 143 - 215 | °C | ISO 306 |
| Melting Temperature | 220 - 243 | °C | ISO 11357-3 |
| CLTE - Flow | 2.0E-5 - 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 - 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+13 - 2.0E+15 | ohms·cm | IEC 60093 |
| Relative Permittivity (23°C) | 3.65 | IEC 60250 | |
| Dissipation Factor (23°C) | 3.0E-3 - 0.021 | IEC 60250 | |
| Comparative Tracking Index | 191 - 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 650 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 675 - 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 - 121 | °C | |
| Drying Time | 2.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Rear Temperature | 250 - 260 | °C | |
| Middle Temperature | 250 - 265 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 80.0 - 95.0 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PBT+ASA - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SuperLite® SL551200-100 (4.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| SUMIKASUPER® LCP E5002L | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| BUPLEN® 6431 | LUKOIL Bulgaria Ltd. | PP Homopolymer | BUPLEN® |
| Ducor® DE1040T | Ducor Petrochemicals BV | PP Homopolymer | Ducor® |
| Pinnacle PP 5120H | Pinnacle Polymers | PP Random Copolymer | Pinnacle PP |