Bergamid™ A700 G15 H BK017
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergamid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | omIRoM_Bergamid-A700-G15-H-BK017.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bergamid™A700 G15 H BK017 is a polyamide 66 (nylon 66) product, which contains a 15% glass fiber reinforced material. It can be processed by injection molding and is available in the Asia-Pacific region. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.60 - 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 5000 | MPa | ISO 178 |
| Flexural Stress | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 230 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.700 mm) | HB | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 260 - 280 | °C | |
| Front Temperature | 260 - 280 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx CPP1B30 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| InnoFR™ FX-8061 | Innovative Polymers, Inc. | TSU | InnoFR™ |
| SQUARE® SSR2026AE/BE | Shenzhen SQUARE Silicone Co., Ltd. | Silicone | SQUARE® |
| EvoSource™ ABS 4136 70/05 | MBA Polymers Austria Kunststoffverarbeitung GmbH | ABS | EvoSource™ |
| POCAN® AF 4130 000000 | LANXESS GmbH | PBT+ASA | POCAN® |