Sindustris ABS LHI221
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | olee53_Sindustris-ABS-LHI221.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris ABS LHI221 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris ABS LHI221 are:
Typical application of Sindustris ABS LHI221: Furniture |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 11 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 87 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 37.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 10 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 1860 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 53.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 400 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 84.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 200 to 220 | °C | |
| Nozzle Temperature | 200 to 230 | °C | |
| Processing (Melt) Temp | 210 to 240 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROLOX GFR 6 | Taro Plast S.p.A. | PBT | TAROLOX |
| DOW™ LDPE PG 7008 (Extrusion Coating) | The Dow Chemical Company | LDPE | DOW™ LDPE |
| BESTNYL SC50VIR34AHM | Triesa Plastics | Nylon 66/6 | BESTNYL |
| Kinta NB2630G | Kinta Technology (Hong Kong) Co., Ltd. | PP, Unspecified | Kinta |
| Sylvin 802-85UV Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |