CYCOLAC™ FR15U resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | olBqG6_CYCOLACFR15Uresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant ABS. Excellent indoor UV properties. Excellent moldability. UL94 V-0/5VA rated.ing. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 3.3 | g/10 min | ASTM D1238 |
| 220°C/5.0 kg | 7.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 40.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2070 | MPa | ASTM D638 |
| -- | 2210 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 37.9 | MPa | ASTM D638 |
| Yield | 41.1 | MPa | ISO 527-2/50 |
| Fracture 3 | 30.3 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield 4 | 2.4 | % | ASTM D638 |
| Fracture 5 | 17 | % | ASTM D638 |
| Fracture | 22 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2340 | MPa | ASTM D790 |
| -- 7 | 2260 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 63.3 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 67.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 210 | J/m | ASTM D256 |
| 23°C 9 | 12 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 28.5 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 86.1 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 75.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 93.9 | °C | ASTM D1525 10 |
| -- | 92.0 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 9.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 9.2E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.20 mm, in Oil) | 20 | kV/mm | IEC 60243-1 |
| Arc Resistance 11 | PLC 7 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.79 mm | 5VA | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (200°C, 1000 sec^-1) | 320 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 87.8 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Shot Size | 50 - 70 | % | |
| Rear Temperature | 171 - 182 | °C | |
| Middle Temperature | 199 - 210 | °C | |
| Front Temperature | 204 - 221 | °C | |
| Nozzle Temperature | 204 - 232 | °C | |
| Processing (Melt) Temp | 204 - 232 | °C | |
| Mold Temperature | 48.9 - 71.1 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 30 - 60 | rpm | |
| Vent Depth | 0.038 - 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 标准 B (120°C/h), 载荷2 (50N) |
| 11 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PH 49 GF 30 TS | Plastcom | PP, Unspecified | SLOVALEN® |
| TOTAL Polypropylene PPH 12020 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Wanthane® WHT-2195 | Wanhua Chemical Group Co., Ltd. | TPU-Capro | Wanthane® |
| Axiall PVC 10852 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Geon™ Vinyl Flexible R5185A | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |