INEOS LDPE 22H760
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | okw4or_INEOS-LDPE-22H760.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
22H760 is an autoclave, low density polyethylene grade for the production of thin blown films. Applications 22H760 is intended for applications such as
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.1 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Film Puncture Energy (40 µm) | 1.30 | J | |
| Film Puncture Force (40 µm) | 50.0 | N | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm | 26.0 | MPa | ISO 527-3 |
| TD : Yield, 40 µm | 20.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 40 µm | 350 | % | ISO 527-3 |
| TD : Break, 40 µm | 60 | % | ISO 527-3 |
| Dart Drop Impact (40 µm) | 100 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40 µm | 5.0 | N | ISO 6383-2 |
| TD : 40 µm | 3.0 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ISO 306 |
| Melting Temperature (DSC) | 111 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (40.0 µm) | 85 | ASTM D2457 | |
| Haze (40.0 µm) | 7.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Tensile Modulus, ASTM D882-A, MD, 40µ: 200 MPaTensile Modulus, ASTM D882-A, TD, 40µ: 210 MPaCoefficient of Friction, ISO 8295, dynamic, 40µ: 0.9The value listed as Melting Point ISO 3146, was tested in accordance with ISO 11357/03.The value listed as Elmendorf Tear Strength ISO 6383-2, was tested in accordance with ISO 8483/2The values listed as Film Puncture Energy and Force, were tested in accordance with ASTM D5748. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 180 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 460.75 HI FR | RTP Company | PS (GPPS) | RTP |
| Staramide R1000K | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| TPC PVC SG660 | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| Karina WHITE PVC COMPOUND 757-10/ 1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ WC006 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |