TRIBOCOMP® PPS CF30 TS0
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | okLZg1_TRIBOCOMP-PPS-CF30-TS0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP®PPS CF30 TS0 is a polyphenylene sulfide (PPS) product, which contains 15% ptfe fiber and 30% carbon fiber reinforced materials. It is available in Europe. The main characteristics are: lubrication. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.57 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 23500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 155 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 21000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 235 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 | ||
| Dynamic | 0.17 | ASTM D3702 | |
| Static | 0.15 | ASTM D3702 | |
| Wear Factor | 70.0 | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 275 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 260 | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 2.2E-5 | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.58 | W/m/K | ISO 22007 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 | ohms | ASTM D257 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 340 - 360 | °C | |
| Middle Temperature | 360 - 380 | °C | |
| Front Temperature | 380 - 390 | °C | |
| Nozzle Temperature | 380 - 390 | °C | |
| Mold Temperature | 160 - 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren F280 (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| VESTAMID® Care ME71 | Evonik Industries AG | PEBA-Ether | VESTAMID® Care |
| Hylon® N1000THLHF2 | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Karina WHITE PVC COMPOUND -E 813-10/164-B-RT-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostacom TKC 156N C12334 | LyondellBasell Industries | PP Copolymer | Hostacom |