HANWHA LLDPE HS1700
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | okCibq_HANWHA-LLDPE-HS1700.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HANWHA LLDPE HS1700 is high strength LLDPE manufactured by Unipol process and designed for stretch wrap and diaper film application. LLDPE HS1600 has excellent mechanical property, stretchability, optical properties and water vapor transmittance rate. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.2 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 34.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 900 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 20 µm | 44.1 | MPa | ASTM D882 |
| TD : Break, 20 µm | 39.2 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 750 | % | ASTM D882 |
| TD : Break, 20 µm | 850 | % | ASTM D882 |
| Dart Drop Impact (20 µm) | 200 | g | ASTM D1709B |
| Tensile Tear Strength | ASTM D1004 | ||
| MD : 20.0 µm | 117.7 | kN/m | ASTM D1004 |
| TD : 20.0 µm | 127.5 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 105 | °C | ASTM D1525 |
| Peak Melting Temperature | 125 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (20.0 µm) | 2.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 270 | °C |
| Extrusion instructions |
|---|
| Optimum Gage Range: 0.015 to 0.05 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds PP-6442 | Ravago Manufacturing Americas, LLC | PP Homopolymer | Ravago Compounds |
| RTP 800 TFE 2 UV | RTP Company | Acetal (POM) Copolymer | RTP |
| XENOY™ X5601WX resin | SABIC Innovative Plastics | PBT+PC+PET | XENOY™ |
| Pinnacle PP 5110H | Pinnacle Polymers | PP Random Copolymer | Pinnacle PP |
| Sylvin 9067-90 RED 6114 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |