LNP™ LUBRILOY™ Lexan_WR6300 compound
| Category: | AES+PC+SAN , Acrylonitrile Ethylene Styrene + PC + SAN |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oirIGg_LNP-LUBRILOY-Lexan-WR6300-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP LUBRILOY LEXAN_WR6300 compound is a wear resistant PC+SAN, with proprietary lubricant, for business equipment applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (300°C/2.16 kg) | 38.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 60.7 | MPa | |
| Break | 61.4 | MPa | |
| Tensile Elongation 2(Break) | 160 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 2490 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 170 | J/m | |
| 23°C | 680 | J/m | |
| Unnotched Izod Impact (23°C) | 2500 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 60.2 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 134 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 117 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 121 | °C | |
| Vicat Softening Temperature | 137 | °C | ASTM D1525 5 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 1.1E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.2E-4 | cm/cm/°C | |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 107 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 227 to 249 | °C | |
| Middle Temperature | 238 to 260 | °C | |
| Front Temperature | 249 to 271 | °C | |
| Nozzle Temperature | 243 to 266 | °C | |
| Processing (Melt) Temp | 249 to 271 | °C | |
| Mold Temperature | 48.9 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RenPIM® VG 5281 Polyol/ 5281 Isocyanate | Huntsman Advanced Materials | PUR, Unspecified | RenPIM® |
| Shin-Etsu Elastomer KE-5560U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| GELAST GT55ISB | Guang Sung Plastics (GSPL) | SEBS | GELAST |
| Jiangsu Sinarise JM7913 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| Lionpol IM-35061 | Lion Polymers Incorporated | TPE | Lionpol |