TOTAL Polyethylene Lumicene® Supertough 32ST05
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oikl7q_TOTAL-Polyethylene-Lumicene-Supertough-32ST05.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lumicene® Supertough 32ST05 is a polyethylene blown film grade that is especially designed to have an excellent processability on extrusion and conversion lines and to give a very high toughness - stiffness balance allowing new innovative multilayer film concepts. Thanks to this innovative design, Lumicene® Supertough 32ST05 brings a huge down-gauging potential in the film market. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.932 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress | |||
| MD : Yield, 40 µm, blown film | 15.5 | MPa | ISO 527-3 |
| TD : Yield, 40 µm, blown film | 16.0 | MPa | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 57.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 48.0 | MPa | ISO 527-3/1B |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 580 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 630 | % | ISO 527-3 |
| Dart Drop Impact (40 µm, Blown Film) | > 280 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 40.0 µm | 55.0 | kN/m | ISO 6383-2 |
| TD : 40.0 µm | 200.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 115 | °C | ISO 306 |
| Melting Temperature | 123 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 14 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 230 | °C |
| Extrusion instructions |
|---|
| BUR: 1.5:1 to 4.5:1Die gap: 1.2 to 2.8 mm |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borlink™ LE4244S | Borealis AG | PE, Unspecified | Borlink™ |
| Diamond HIPS HI-861 | Diamond Polystyrene | PS (HIPS) | Diamond HIPS |
| Plaslube® J-80/20/TF/15 NAT | Techmer Engineered Solutions | Acetal (POM) Copolymer | Plaslube® |
| POLYFLON™ L-5F | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |
| Sumiliteresin® PR-50064 I | SBHPP | Phenolic | Sumiliteresin® |