RTP 154 HF HI
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ohsGmr_RTP-154-HF-HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Copolymer - High Flow - Flame Retardant |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 35 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.5 to 2.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1170 | MPa | ASTM D638 |
| Tensile Strength | 17.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 100 | % | ASTM D638 |
| Flexural Modulus | 896 | MPa | ASTM D790 |
| Flexural Strength | 22.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 590 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 1400 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 40.6 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm, ** Values per RTP Company testing. | V-0 | ||
| 0.200 mm, ** Values per RTP Company testing. | VTM-0 | ||
| Oxygen Index | 27 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 191 to 232 | °C | |
| Mold Temperature | 32.2 to 65.6 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Topolymer® 8209-P | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| ALCOM® PA66 910/1 GF30 MO2 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| EMLON® 66 | EMAS Plastik San.Tic.AS. | Nylon 66 | EMLON® |
| LEXAN™ EXL8454 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Braskem PP DR155.01 | Braskem Europe GmbH | PP Random Copolymer | Braskem PP |