LNP™ VERTON™ RX89047 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ogzI69_LNPVERTONRX89047compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON RX89047 is a compound based on Nylon 66 resin. Also known as: LNP* VERTON* Compound PDX-R-89047 Product reorder name: RX89047 |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.42 | g/cm³ | ASTM D792 |
| -- | 1.41 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 11400 | MPa | ASTM D638 |
| Tensile Strength | |||
| Fracture | 202 | MPa | ASTM D638 |
| Fracture | 198 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 2.3 | % | ASTM D638 |
| Fracture | 200 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9650 | MPa | ASTM D790 |
| -- | 9500 | MPa | ISO 178 |
| Flexural Strength | 317 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 360 | J/m | ASTM D256 |
| 23°C 2 | 24 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 1000 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 253 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 3 | 251 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000 GV 35 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Akulon® Ultraflow K-FG0 | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |
| Karina PVC COMPOUND BLACK E-550-D48/1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ WG003 compound | SABIC Innovative Plastics Europe | PBT | LNP™ LUBRICOMP™ |
| TECHNYL® C 230 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |