Ultrason® S 2010 G4
| Category: | PSU , Polysulfone |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultrason® S |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ogsRIX_Ultrason-S-2010-G4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultrason S 2010 G4 is a 20% glass reinforced, medium viscosity injection molding PSU grade with high rigidity and strength. Applications Typical applications include circuit braker parts, lamp holders, heat shields, impellers, and printer cartridges. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (360°C/10.0 kg) | 40.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.52 | % | |
| Flow | 0.31 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.70 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 170 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6600 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.9 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 55 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 184 | °C | ISO 75-2/A |
| CLTE - Flow | 2.6E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | ||
| 1.60 mm | 160 | °C | |
| 3.00 mm | 160 | °C | |
| RTI Imp | UL 746 | ||
| 1.60 mm | 140 | °C | |
| 3.00 mm | 140 | °C | |
| RTI Str | UL 746 | ||
| 1.60 mm | 160 | °C | |
| 3.00 mm | 160 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 46 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.50 | ||
| 1 MHz | 3.50 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.0E-3 | ||
| 1 MHz | 6.0E-3 | ||
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-1 | ||
| 3.00 mm | V-0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene F15-00UV | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| NEFTEKHIM PS 404 | Nizhnekamskneftekhim Inc. | PS (GPPS) | NEFTEKHIM PS |
| Novalloy-B B1400MM | PlastxWorld Inc. | ABS+PBT | Novalloy-B |
| LUVOCOM® 1105-8416 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Plexiglas® 8H | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |