ACRYPET® VH
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Mitsubishi Rayon Co., Ltd. |
| Trademark: | ACRYPET® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ogfp0e_ACRYPET-VH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Acrypet®VH is a polymethyl methacrylate-acrylic material,. This product is available in North America,. Acrypet®The main features of VH are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 - 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 72.4 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus (6.35 mm) | 3140 | MPa | ASTM D790 |
| Flexural Strength (6.35 mm) | 108 | MPa | ASTM D790 |
| Compressive Strength | 108 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 17 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 102 | °C | ASTM D648 |
| Vicat Softening Temperature | 116 | °C | ASTM D1525 |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance (3200 µm) | 93.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Surface Resistivity, JIS K6911: >10^16 ohmVolume Resistivity, JIS K6911: >10^15 ohm-cmDielectric Breakdown Strength: 20 kV/mmDielectric Constant, 60Hz: 3.7Dielectric Loss Tangent, 60Hz: 0.05Arc Resistance, JIS K6911: No Trace |
| Note Message | |
|---|---|
| 1 . | Type 1 |
| 2 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 66 Prime Series PGF50-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| APEX® 75-9351A-102 | Teknor Apex Company | PVC, Flexible | APEX® |
| Desmopan® DP 3072D | Covestro - PUR | TPU-Polyester | Desmopan® |
| EVALENE® LLDPE LF20184 | JG Summit Petrochemical Corporation | LLDPE | EVALENE® LLDPE |
| Braskem PP TI6500WV | Braskem America Inc. | PP Impact Copolymer | Braskem PP |