ELEVATE™ EF524
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | ELEVATE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ogcOYf_ELEVATE-EF524.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Westlake ELEVATE™ EF524 is an ethylene vinyl acetate copolymer with 14.5% VA. EF524 is designed for blown and cast filmsrequiring excellent optics and low heat seal initiation. High melt strength makes EF524 an excellent choice for profile extrusions, molding, and foaming applications requiring high VA content. Application/Uses: Flexible packaging films Peelable seals, adhesive layers Injection and blow molding Profile extrusions, tubing, wire & cable |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.934 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | 3.5 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 14.5 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD : 51 µm, blown film | 51.7 | MPa | ASTM D882 |
| 1% secant, TD : 51 µm, blown film | 55.2 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Broken, 51 µm, blown film | 22.1 | MPa | ASTM D882 |
| TD : Broken, 51 µm, blown film | 20.7 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 51 µm, blown film | 700 | % | ASTM D882 |
| TD : Broken, 51 µm, blown film | 1000 | % | ASTM D882 |
| Dart Drop Impact 4(51 µm, Blown Film) | 380 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 67.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 90.0 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 5(45°, 50.8 µm, Blown Film) | 87 | ASTM D2457 | |
| Haze 6(50.8 µm, Blown Film) | 1.5 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blown Film Melt Temperature | °C | ||
| Cast Film Melt Temperature | °C | ||
| Typical film properties as measured on a 2.0 mil blown film sample fabricated at a 2.5:1 B.U.R. |
| Note Message | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | Test run at 23°C (73°F) and 50% relative humidity |
| 5 . | As measured on AA formulation which contains no slip and no antiblock. |
| 6 . | As measured on AA formulation which contains no slip and no antiblock. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTS POM-90 | Polymer Technology and Services, LLC | Acetal (POM) Copolymer | PTS |
| AEI TP-0832 | AEI Compounds Limited | PE, Unspecified | AEI |
| Interpol 47-5132/47-5205 | Cook Composites and Polymers | PUR-Ester | Interpol |
| Karina ORANGE COLOR CONCENTRATE 32/1-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TECACOMP® PPS HTE black 3986V | Ensinger GmbH | PPS | TECACOMP® |