Maxxam™ H6 GF/30 H Black
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ogOz5I_MaxxamH6GF30HBlack.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium carbonate, glass and talc to provide a desired balance of properties including stiffness, durability, impact resistance and heat resistance. Custom grades are available with features such as UV stabilizers, heat stabilizers, custom color, high impact, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1(23°C) | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 6.00 | cm³/10min | ISO 1133 |
| Shrinkage- Lateral flow 2(23°C, 2.00 mm) | 0.30 - 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm, Injection Molded) | 5500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C, 4.00 mm) | 70.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C, 4.00 mm) | 3.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 11 | kJ/m² | ISO 180/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.6 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | ±0.03 g/cm³ |
| 2 . | Internal Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® F02-137D | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TOTAL Polypropylene PPC 4624WZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Bayfill® 53IF40 U | Covestro - PUR | PUR, Unspecified | Bayfill® |
| Fainplast PVC GS 66/BT | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Gallonprene® GP410-9003 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |