SABIC® PPcompound 7500
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ofhvGi_SABIC-PPcompound-7500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 7500 is a mineral filled modified polypropylene. This material combines high flow, good impact and a high stiffness level with a low shrinkage and CLTE. Typical applications include automotive exterior parts such as large thin wall zero gap bumper designs but also lateral siding and bumper strips. It can be used in painted and unpainted applications with UV stabilization added on demand. SABIC® PPcompound 7500 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.90 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 20.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 17.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 500 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 1300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength (-40°C, Injection Molded) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 6.0 | kJ/m² | |
| 0°C, Injection Molded | No Break | ||
| 23°C, Injection Molded | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 100 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 130 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 7.5E-5 | cm/cm/°C | |
| 23 to 80°C | 1.0E-4 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier LB02019 - D | Premier Polymers, LLC. | LLDPE | Premier |
| Sinvicomp SGH6500 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| TROGAMID® CX CX9704 | Evonik Industries AG | Nylon, Unspecified | TROGAMID® CX |
| ColorFast® FRPE200 | LTL Color Compounders, Inc. | LDPE | ColorFast® |
| Karina WHITE PVC COMPOUND 805-10/152-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |