VECTRA® MT1335
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oei1rN_VECTRA-MT1335.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Best High Current Arc Ignition (HAI) performance. Glass/PTFE filled. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant Celanese has established at the FDA a drug master file (DMF no.8468) and a Device Master File (MAF no.315) for Vectra MT1335. These are to assist our customers with their end use FDA petitions. Vectra MT1335 has been tested and complies with USP Class VI. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.62 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.40 | % | ISO 294-4 |
| Flow direction | 0.10 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 55 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 171 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.3 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 10500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 206 | MPa | ISO 178 |
| Compressive Modulus | 10500 | MPa | ISO 604 |
| Compressive Stress (1% Strain) | 77.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 26 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 38 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 17 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 33 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 250 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 230 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 162 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 146 | °C | ISO 306/B50 |
| Melting Temperature 1 | 280 | °C | ISO 11357-3 |
| CLTE - Transverse | 1.9E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 32 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.50 | IEC 60250 | |
| 1 MHz | 3.10 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.020 | IEC 60250 | |
| 1 MHz | 0.016 | IEC 60250 | |
| Arc Resistance | 130 | sec | Internal method |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 275 - 285 | °C | |
| Front Temperature | 280 - 290 | °C | |
| Nozzle Temperature | 290 - 300 | °C | |
| Processing (Melt) Temp | 285 - 295 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 150 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 285 to 295°CZone 4 Temperature: 285 to 295°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4085 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| PTS PBT-30GF | Polymer Technology and Services, LLC | PBT | PTS |
| Unichem 9812-15 | Colorite Polymers | PVC, Unspecified | Unichem |
| Chemlon® 120 G | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Hytrel® HTR8223 BK320 | DuPont Performance Polymers | TPC-ET | Hytrel® |