LNP™ STAT-KON™ DD000 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | odnffN_LNPSTATKONDD000compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* DD000 is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound D Product reorder name: DD000 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.80 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.80 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.82 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.84 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.14 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.25 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2690 | MPa | ASTM D638 |
| -- | 2900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 62.9 | MPa | ASTM D638 |
| Yield | 60.6 | MPa | ISO 527-2 |
| Fracture | 56.3 | MPa | ASTM D638 |
| Fracture | 53.7 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 4.9 | % | ASTM D638 |
| Yield | 4.4 | % | ISO 527-2 |
| Fracture | 9.5 | % | ASTM D638 |
| Fracture | 8.8 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2900 | MPa | ASTM D790 |
| -- | 3100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 102 | MPa | ASTM D790 |
| -- | 103 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 64 | J/m | ASTM D256 |
| 23°C 2 | 6.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1200 | J/m | ASTM D4812 |
| 23°C 3 | 99 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 8.40 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 138 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 128 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 127 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylink Polymer P-51030-GF(N) | Polylink Polymers (India) Ltd. | Nylon 6 | Polylink Polymer |
| Shanghai Potomer SG3 | Shanghai Potomer International Trade Co., Ltd. | PVC, Flexible | Shanghai Potomer |
| Skyrol® SH32 | SKC Inc. | PET | Skyrol® |
| Axiall PVC 8916 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Sylvin 9067A-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |