OnForce™ LFT LF5200-5017 Grey
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | PolyOne Corporation |
| Trademark: | OnForce™ LFT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | odD0F2_OnForceLFTLF52005017Grey.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Edgetek®The engineering thermoplastic polymer product portfolio includes a series of standard and customizable high-performance materials. The combination includes high-temperature resistant materials for high-temperature working environments, and high-modulus/structural materials for load-bearing, high-strength applications and flame-retardant products. These polymers are made by mixing engineering thermoplastic resins with different reinforcing additives, such as carbon fiber, glass fiber and glass beads. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.990 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 0.30 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 180 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.7 | % | ISO 527-2 |
| Flexural Modulus | 9500 | MPa | ISO 178 |
| Flexural Stress | 195 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 9.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 35 | kJ/m² | ISO 179 |
| Dart Drop Impact | 45.0 | J | ASTM D5420 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 210 - 230 | °C | |
| Mold Temperature | 60 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 1.00 | MPa |
| Injection instructions |
|---|
| LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed. |
| Note Message | |
|---|---|
| 1 . | Measured on a tensile specimen. Actual mold shrinkage values are highly dependant on part geometry, mold configuration, and processingconditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE ML-1533N | Teknor Apex Company | TPE | Sarlink® TPE |
| Sylvin 2900-65 Clear | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| ENVIROPLAS® ENV17-NC060 | ENVIROPLAS®, Inc. | PEI | ENVIROPLAS® |
| MAJORIS EE115T - 8938 | AD majoris | PP, Unspecified | MAJORIS |
| ESTOPLAST SR 1500BG73 | Ester Industries Ltd. | ABS | ESTOPLAST SR |