TEKNIFLEX® VDC 200-25-60
| Category: | Film, PVC/PE/PVDC , PVC/PE/PVDC Film |
| Manufacturer: | Tekni-Films, a div of Tekni-Plex |
| Trademark: | TEKNIFLEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ocpsMw_TEKNIFLEX-VDC-200-25-60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoformable, FDA-compliant, Pharmaceutical-grade PVC/PE/PVdC film. Tekni-Plex offers a wide range of PVDC-based film structures to meet both performance and cost requirements. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | |
| Dimensional Stability 1(140°C) | -4.0 to 4.0 | % |
| Films | Nominal Value | Unit | |
|---|---|---|---|
| Film Thickness 2 | 260 | µm | |
| Yield | 2.76 | m²/kg |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Roll Width 3 | < 110.00 | cm | |
| Thermoforming Molding Temperature | 100 to 160 | °C |
| Films | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength - MD (Yield) | 34.5 | MPa | |
| Oxygen Transmission Rate (23°C, 100% RH) | 0.50 | cm³/m²/24 hr | |
| Water Vapor Transmission Rate (38°C, 90% RH) | 0.50 | g/m²/24 hr |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Haze | 5.0 | % |
| Note Message | |
|---|---|
| 1 . | 30 minutes |
| 2 . | Thickness tolerance: ±7% |
| 3 . | Roll width tolerance: ±1.5 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-9710U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| ColorRx® PCT-1500RX | LTL Color Compounders, Inc. | PC+PET | ColorRx® |
| Formolene® 6510A | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| LG PS 15NFI | LG Chem Ltd. | PS (GPPS) | LG PS |
| LUVOCOM® 1301-VAP 10 | LEHVOSS Group | PPS | LUVOCOM® |