Ecovio® T2308
| Category: | Copolyester , Copolyester |
| Manufacturer: | BASF Corporation |
| Trademark: | Ecovio® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ocdNw4_Ecovio-T2308.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ecovio® T 2308 is a biodegradable film product containing renewable resources. It is basically a compound of our biodegradable copolyester ecoflex® and polylactic acid (PLA). Because of the PLA content ecovio® T 2308 consists of 80% of renewable resources. PLA is the continuous phase in the structure of ecovio® T 2308 transferring the beneficial properties of ecoflex® into the new product. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 to 1.26 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/5.0 kg) | 7.50 to 11.5 | cm³/10min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-3 | ||
| MD : 1000 µm | 2680 | MPa | |
| TD : 1000 µm | 2240 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 1000 µm | 27.0 | MPa | |
| TD : Break, 1000 µm | 20.0 | MPa | |
| MD : 1000 µm | 56.0 | MPa | |
| TD : 1000 µm | 40.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 1000 µm | 56 | % | |
| TD : Break, 1000 µm | 38 | % | |
| Water Vapor Transmission Rate (1000 µm) | 3.8 | g/m²/24 hr | ASTM F1249 |
| Oxygen Permeability (1.00 mm) | 32 | cm³/m²/bar/24 hr | ASTM D3985 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Renewable Content | 80 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 55.0 | °C | ISO 306/B50 |
| Melting Temperature | DSC | ||
| -- 1 | 110 to 120 | °C | |
| -- 2 | 140 to 155 | °C |
| Note Message | |
|---|---|
| 1 . | ecoflex® |
| 2 . | PLA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III HDPERBI 8.0 | ROMPETROL PETROCHEMICALS S.R.L. | HDPE | MIDILENA III |
| Mowiol® 10-98 | Kuraray Co., Ltd. | PVOH | Mowiol® |
| TITANPRO® EPC40R | Lotte Chemical Titan (M) Sdn. Bhd. | PP Impact Copolymer | TITANPRO® |
| K-Flex EL 37 FR | Technovinyl Polymers India Ltd. | PVC Elastomer | K-Flex |
| HiFill® XMD POM 0167 LE | Techmer Engineered Solutions | Acetal (POM) Copolymer | HiFill® |