Anjacom® 055/80-GF20 Black 91220
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Almaak International GmbH |
| Trademark: | Anjacom® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | obS6bx_Anjacom-055-80-GF20-Black-91220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Anjacom® 055/80-GF20 Black 91220 is a Polycarbonate + ABS (PC+ABS) material filled with 20% glass fiber. It is available in Europe for injection molding. Primary attribute of Anjacom® 055/80-GF20 Black 91220: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.25 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.20 to 0.50 | % | |
| Flow | 0.30 to 0.60 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.60 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 124 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 137 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4007 UP | RTP Company | PPA | RTP |
| 4MID® 9B22115 FR5L-S | 4Plas | Nylon 6 | 4MID® |
| EPO-TEK® H37-MP | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Jamplast JPLGABSI | Jamplast, Inc. | ABS | Jamplast |
| LNP™ STAT-KON™ DD0009 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |