Paryls® mPPSU M1150
| Category: | PPSU, Modified , Modified Polyphenylsulfone |
| Manufacturer: | Youju New Materials Co., Ltd. |
| Trademark: | Paryls® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oarcpp_ParylsmPPSUM1150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PARYLS® mPPSU M1150 pellets are supplied in cartons lining aluminum foil bag, which can be stored indefinitely, provided the packaging remains undamaged. PARYLS® mPPSU M1150 pellets absorb moisture very rapidly. Therefore, the pellets need to be dried at least 6h at 160 °C in a vacuum or dry air drier prior to processing. Features PARYLS® mPPSU is a modified polyphenylsufone. It is a high-heat, high performance resin formulation exhibiting very good hydrolytic stability, excellent resistance to scids and bases and good resistance to stress cracking under a broad range of chemical environments. In addition, PARYLS® mPPSU resin exhibits robust toughness and improved notch resistance compared to both PARYLS® PSU and PARYLS® PES, although slightly lower than that of neat PARYLS® PPSU. In general, the performance profile of PARYLS® mPPSU resin falls between PSU and PPSU, and also offers very good electrical properties over a broad temperature range as well as inherent flam retardancy, offers better cost-efficiency advantage also. Natural: mPPSU M1150NT, Black: mPPSU M1150BK, White: mPPSU |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (380°C/2.16 kg) | 15 - 20 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4, ISO 2577 | ||
| Transverse flow | 0.80 | % | ISO 294-4, ISO 2577 |
| Flow | 0.70 | % | ISO 294-4, ISO 2577 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2690 | MPa | ISO 527-2 |
| Tensile Stress | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 7.0 | % | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Stress | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 10 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 195 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 1 | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity 2 | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 44 | kV/mm | ASTM D149 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.80 | IEC 60250 | |
| 1 MHz | 3.70 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.5E-3 | IEC 60250 | |
| 1 MHz | 8.6E-3 | IEC 60250 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 160 | °C | |
| Drying Time | 6.0 | hr | |
| Processing (Melt) Temp | 350 - 390 | °C | |
| Mold Temperature | 140 - 160 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 160 | °C | |
| Drying Time | 6.0 | hr | |
| Melt Temperature | 350 - 390 | °C | |
| Die Temperature | 140 - 160 | °C |
| Note Message | |
|---|---|
| 1 . | 100V |
| 2 . | 100V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Celstran® PA66-GF60-02-Natural | Celanese Corporation | Nylon 66 | Celstran® |
| DIALAC® ESA30 | UMG ABS, Ltd. | AES | DIALAC® |
| Formolene® 6375N | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| ELASTOSIL® SOLAR 1109 WHITE | Wacker Chemie AG | Silicone | ELASTOSIL® SOLAR |
| ELASTOSIL® RT 601 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® RT |