Order Products : sales@su-jiao.com

EMAC+® SP1307

Category:	EMA , Ethylene Methyl Acrylate Copolymer
Manufacturer:	Westlake Chemical Corporation
Trademark:	EMAC+®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	oZvLiC_EMAC-SP1307.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
EMAC resins adhere to and are compatible with a wide range of materials including paper, polyolefins, oriented polyolefins, polyesters, ionomers, PVdC, unplasticized PVC and other polar polymers. For use as heat seal layer, adhesive layer, or modifier for cost/performance enhancement. They are soft, pliable and tough at ambient and freezing temperatures and exhibit excellent ESCR. These polymers exhibit high solids fillability and compatibility with a wide range of polymers. This facilitates their uses as bases for all-purpose concentrates for addition to a wide spectrum of polymers. EMAC resins process like LDPE. EMAC+ Specialty Copolymers are produced under patented technology: US Patent 5804675.

Message

EMAC resins adhere to and are compatible with a wide range of materials including paper, polyolefins, oriented polyolefins, polyesters, ionomers, PVdC, unplasticized PVC and other polar polymers. For use as heat seal layer, adhesive layer, or modifier for cost/performance enhancement. They are soft, pliable and tough at ambient and freezing temperatures and exhibit excellent ESCR. These polymers exhibit high solids fillability and compatibility with a wide range of polymers. This facilitates their uses as bases for all-purpose concentrates for addition to a wide spectrum of polymers. EMAC resins process like LDPE. EMAC+ Specialty Copolymers are produced under patented technology: US Patent 5804675.

General Information
Features	Good Adhesion Good Flexibility Good Heat Seal Good Toughness High ESCR (Stress Crack Resist.) Soft
Uses	Film Tie-Layer

Physical	Nominal Value	Unit	Test Method
Density	0.942	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	6.0	g/10 min	ASTM D1238
Methyl Acrylate Content	20.0	wt%

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	35		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Break)	10.0	MPa	ASTM D638
Tensile Elongation ²(Break)	830	%	ASTM D638

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -73.0	°C	ASTM D746
Vicat Softening Temperature	46.0	°C	ASTM D1525
Peak Melting Temperature	95.0	°C	ASTM D3418

Note Message
1 .	Type IV, 500 mm/min
2 .	Type IV, 500 mm/min

Resin Grade	Manufacturer	Category	Trademark
Toyolac® 440Y-X01	Toray Resin Company	ABS	Toyolac®
Witcom PA6 EC-HI	Witcom Engineering Plastics B.V.	Nylon 6	Witcom PA6
Badadur® PBT9 FR HF	Bada AG	PBT	Badadur®
Sylvin 916VO Grey 950	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
POCAN® B 1300 000000	LANXESS Corporation	PBT	POCAN®